Synthesis of fibroin/silica adsorbent for thin layer chromatography
DOI:
https://doi.org/10.15407/hftp17.02.241Keywords:
fibroin, tetraethoxysilane, sol-gel process, nanohybridє, polycondensation, fibroin/silica adsorbent, hybrid material, thin-layer chromatography, ortho-nitroaniline, meta-nitroaniline, para-nitroanilineAbstract
The main aim of this work is to synthesize microspherical fibroin/silica adsorbent through a one-step in situ synthesis that integrates silk fibroin into the hydrolytic polycondensation of tetraethoxysilane (TEOS). The kinetics of the sol-gel process is studied at varying ratios of the initial reagents - fibroin, TEOS and ammonium hydroxide in a 4% formic acid solution under different temperatures and stirring rates. It was demonstrated that the sol-gel transition in all cases occurs within a few minutes. The highest yield of the target product was observed at a fibroin:TEOS ratio of 0.03:1 and the addition of 2.3 ml of 25 % ammonium hydroxide solution. The obtained samples were analyzed using scanning electron microscopy with EDS, nitrogen porosimetry, IR spectroscopy, diffractometry and thermogravimetry. The morphologically obtained fibroin/silica adsorbent consists of microspherical particles measuring 10 ?m in size, with a pore size distribution of 10–30 nm and a specific surface area of 318 m2·g-1. The IR study of the obtained nanohybrid fibroin/silica adsorbent reveals absorption bands at 3410 cm–1 characteristics of ?Si-OH groups and at 1063 cm–1 related to vibrations of the siloxane group ?Si-O-Si? in the silica structure. The characteristic absorption bands of Amide I at 1638 cm–1 and Amide II at 1512 cm–1 confirm the presence of fibroin. The interactions between fibroin macromolecules and the formed silica structure are evidenced by a reduction in crystallinity of the fibroin within the obtained samples. The nitrogen adsorption and desorption isotherm reveals the presence of a hysteresis loop, indicating that the obtained nanohybrid fibroin/silica adsorbent possesses the mesoporous structure. According to the IR spectral, X-ray structural and thermal characteristics, the obtained product comprises silica and fibroin phases and differs from its constituent components, which confirm its nature as a hybrid nanocomposite material. Additionally, its potential application for separating nitroaniline isomers using high-performance thin-layer chromatography has been demonstrated.
References
1. Hardy J.G., Scheibel T.R. Composite materials based on silk proteins. Progress in Polymer. 2010. 35(9): 1093. https://doi.org/10.1016/j.progpolymsci.2010.04.005
2. Xu Z. Y., Li Y. H., Wang L.J. Versatile technique to functionalize optical microfibers via a modified sol-gel dip-coating method. Opt. Lett. 2014. 39(1): 34. https://doi.org/10.1364/OL.39.000034
3. Lee A., Elam J.W., Darling S.B. Membrane materials for water purification: Design, development, and application. Environ. Sci. Water Res. Technol. 2016. 2(1): 7. https://doi.org/10.1039/C5EW00159E
4. Zhang X., Ding Sh., Tang Z., Yao Z., Zhang T., Xiang C. Nanostructured materials for next-generation display technology. Nat. Rev. Electr. Eng. 2025. 2: 263. https://doi.org/10.1038/s44287-025-00158-6
5. Chirila T.V. Oxygen Permeability of Silk Fibroin Hydrogels and Their Use as Materials for Contact Lenses: A Purposeful Analysis. Gels. 2021. 7(2): 58. https://doi.org/10.3390/gels7020058
6. Khan R.S., Rather A.H., Wani T.U., Rather S., Amna T., Hassan M.Sh., Sheikh F.A. Recent trends using natural polymeric nanofibers as supports for enzyme immobilization and catalysis. Biotechnology Bioengineering. 2023. 120(1): 22. https://doi.org/10.1002/bit.28246
7. Pritchard E.M., Kaplan D.L. Silk fibroin biomaterials for controlled release drug delivery. Expert Opin. Drug Deliv. 2011. 8(6): 797. https://doi.org/10.1517/17425247.2011.568936
8. Lawrence B.D., Marchant J.K., Pindrus M.A., Omenetto F.G., Kaplan D.L. Silk film biomaterials for cornea tissue engineering. Biomaterials. 2009. 30(7): 1299. https://doi.org/10.1016/j.biomaterials.2008.11.018
9. Kabulov B.D., Grabovskaya T.A., Zalyalieva S.V. Microspherical silica gel for high-performance liquid chromatography. Russ. J. Phys. Chem. 1993. 67(10): 2070. [in Russian].
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2026 Д.Ш. Шакарова, Ч.К. Бегімкулова
This work is licensed under a Creative Commons Attribution 4.0 International License.
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
- Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work.