The aim of the work is to compare the microporous structure characteristics of activated carbons (ACs) prepared from coals of different coals rank (CR) by alkaline activation (R_KOH = 1 g/g, 800 °C) and to determine the ACs capability to adsorb phenol and 4-chlorophenol from aqueous solutions.

Starting materials are coals with increasing carbon content (C^daf = 80.0–95.6 %) selected as a CR criterion. ACs were obtained in argon in three stages: 1) thermoprogrammed heating (4 grad/min) to 800 °С; 2) isothermal exposure 1 h; 3) cooling, washing from alkali and drying. Based on low-temperature (77 K) nitrogen adsorption-desorption isotherms, integral and differential dependences of the specific surface area S (m²/g) and pore volume V (cm³/g) on the average pore diameter (D, nm) were calculated. They were used to define volumes of ultramicropores (V_umi), supermicropores (V_smi) and micropores (V_mi). The total pore volume V_t was calculated from the nitrogen amount adsorbed at a relative pressure p/p₀ ~ 1.0. The S values of ultramicropores (S_umi), supermicropores (S_smi) and micropores (S_mi) were similarly determined.

The volumes and specific surfaces of different categories of pores were found to decrease with CR increase: volume V_t – from 0.59 to 0.23 cm³/g; V_mi – from 0.51 to 0.17 cm³/g; the ultramicropores volume – from 0.31 cm³/g to zero in anthracite AC. The supermicropores volume is almost independent on CR and varies in the wide range V_smi = 0.15–0.22 cm³/h. The specific surface area is the maximum (S = 1547 m²/g) in AC from the coal of the lowest CR and decreases with coal metamorphism up to 322 m²/g. The micropores surfaces make dominant contributions to the S values: its portion is 94.7–99.4 %. For all ACs, the adsorption of phenol (Ph) and 4-chlorophenol (CPh) from aqueous solutions at 25 °C was studied. Adsorption kinetics and isotherms are best described by the pseudo-second order model and the Langmuir model (R² ≥ 0.998). With increasing CR, the maximum adsorption capacities decrease from 3.113 to 1.498 mmol/g (Ph) and from 3.9 to 2.1 mmol/g (CPh), that is approximately ~2 times when the specific surface area decreases by ~5 times. The Ph and CPh specific capacities, characterizing the adsorption capacity of 1 m² of surface, change little at C^daf≤86 %, but markedly increase (2.3–2.5 times) for anthracite AСs. The Ph and CPh capacitances were determined to increase linearly (R² ≥ 0.966) with increasing ACs specific surface area. Similar dependences were found on the S_umi and S_mi parameters. The phenols were concluded to be equally adsorbed on the surface of pores of any size. A general trend was found for ACs from hard coals and anthracite: an increase in CR reduces the ACs microporosity and surface, decreases Ph and CPh capacities but increases specific capacities, i.e. concentrations of surface adsorption centers. The Ph and CPh adsorption was accepted to include the interaction of π-electrons of phenolic rings and π-electrons of graphene layers in ACs, the formation of complexes with surface groups and forming hydrogen bonds with OH-groups. Their contributions depend on adsorbate nature and change with the growth of fossil coals CR.

Xing B.-L., Guo H., Chen L.-J., Chen Z.-F., Zhang C.-X., Huang G.-X., Xie W., Yu J.-L. Lignite-derived high surface area mesoporous activated carbons for electrochemical capacitors. Fuel Process. Technol. 2015. 138: 734. https://doi.org/10.1016/j.fuproc.2015.07.017

Zhao X.-Y., Huang S.-S., Cao J.-P., Xi S.-C., Wei X.-Y., Kamamoto J., Takarada T. KOH activation of a HyperCoal to develop activated carbons for electric double-layer capacitors. J. Anal. Appl. Pyrolysis. 2014. 105: 116. https://doi.org/10.1016/j.jaap.2013.10.010

Chesnokov N.V., Mikova N.M., Ivanov I.P., Kuznetsov B.N. Synthesis of carbon sorbents by chemical modification of fossil coals and plant biomass. Journal of Siberian Federal University. Chemistry. 2014. 7(1): 42.

Murali S., Potts J.R., Stoller S., Park J., Stoller M.D., Zhang L., Zhu Y., Ruoff R.S. Preparation of activated graphene and effect of activation parameters on electrochemical capacitance. Carbon. 2012. 50(10): 3482. https://doi.org/10.1016/j.carbon.2012.03.014

Mochizuki T., Kubota M., Matsuda H., D'Elia Camacho L.F. Adsorption behaviors of ammonia and hydrogen sulfide on activated carbon prepared from petroleum coke by KOH chemical activation. Fuel Process. Technol. 2016. 144: 164. https://doi.org/10.1016/j.fuproc.2015.12.012

Ganesan A., Shaijumon M.M. Activated graphene-derived porous carbon with exceptional gas adsorption properties. Microporous Mesoporous Mater. 2016. 220: 21. https://doi.org/10.1016/j.micromeso.2015.08.021

Heimböckel R., Kraas S., Hoffmann F., Fröba M. Increase of porosity by combining semi-carbonization and KOH activation of formaldehyde resins to prepare high surface area carbons for supercapacitor applications. Appl. Surf. Sci. 2018. 427: 1055. https://doi.org/10.1016/j.apsusc.2017.08.095

Javed H., Luong D.X., Lee C.-G., Zhang D., Tour J.M., Alvarez P.J.J. Efficient removal of bisphenol-A by ultra-high surface area porous activated carbon derived from asphalt. Carbon. 2018. 140: 441. https://doi.org/10.1016/j.carbon.2018.08.038

Wei F., Zhang H., He X., Ma H., Dong S., Xie X. Synthesis of porous carbons from coal tar pitch for high-performance supercapacitors. New Carbon Materials. 2019. 34(2): 132. https://doi.org/10.1016/S1872-5805(19)60006-5

Chen W., Luo M., Yang K., Zhou X. Microwave-assisted KOH activation from lignin into hierarchically porous carbon with super high specific surface area by utilizing the dual roles of inorganic salts: Microwave absorber and porogen. Microporous Mesoporous Mater. 2020. 300: Article 110178. https://doi.org/10.1016/j.micromeso.2020.110178

Tiwari D., Bhunia H., Bajpai P.K. Adsorption of CO2 on KOH activated, N-enriched carbon derived from urea formaldehyde resin: kinetics, isotherm and thermodynamic studies. Appl. Surf. Sci. 2018. 439: 760. https://doi.org/10.1016/j.apsusc.2017.12.203

Jordá-Beneyto M., Suárez-García F., Lozano-Castelló D., Cazorla-Amorós D., Linares-Solano A. Hydrogen storage on chemically activated carbons and carbon nanomaterials at high pressures. Carbon. 2007. 45(2): 293. https://doi.org/10.1016/j.carbon.2006.09.022

Vilaplana-Ortego E., Lillo-Ródenas M.A., Alcañiz-Monge J., Cazorla-Amorós D., Linares-Solano A. Isotropic petroleum pitch as a carbon precursor for the preparation of activated carbons by KOH activation. Carbon. 2009. 47(8): 2141. https://doi.org/10.1016/j.carbon.2009.04.020

Kucherenko V.O., TamarkinaYu.V., Popov A.F. Thermal shock alkali activation - a new method of preparation nanoporous carbon adsorbents. Dopovidi NAN Ukrainy. 2016. 12: 74. [in Ukrainian]. https://doi.org/10.15407/dopovidi2016.12.074

Kucherenko V.A., Tamarkina Yu.V., Frolova I.B., Chernyschova M.I., Saberova V.A. Reorganization of black coals structure during the impregnation by potassium hydroxide. Coal Chemistry Journal. 2017. 19(1-2): 10. [in Russian].

Kucherenko V.A., Tamarkina Yu.V., Rayenko G.F. Potassium hydroxide influence on the strucrute and surface area development of brown coal under alkali activation. Him. Fiz. Tehnol. Poverhni. 2017. 8(2): 133. [in Russian]. https://doi.org/10.15407/hftp08.02.133

Jagiello J. Olivier J.P. 2D-NLDFT adsorption models for carbon slit-shaped pores with surface energetical heterogeneity and geometrical corrugation. Carbon. 2013. 55: 70. https://doi.org/10.1016/j.carbon.2012.12.011

Wu J., Montes V., Virla L.D., Hill J.M. Impacts of amount of chemical agent and addition of steam for activation of petroleum coke with KOH or NaOH. Fuel Process. Technology. 2018. 181: 53. https://doi.org/10.1016/j.fuproc.2018.09.018

Thommes M., Kaneko K., Neimark A.V., Olivier J.P., Rodriguez-Reinoso F., Rouquerol J., Sing K.S.W. Physisorption of gases, with special reference to the evaluation of surface area and pore size distribution (IUPAC Technical Report). Pure Appl. Chem. 2015. 87(9-10): 1051. https://doi.org/10.1515/pac-2014-1117

Lorenc-Grabowska E., Rutkowski P. High basicity adsorbents from solid residue of cellulose and synthetic polymer co-pyrolysis for phenol removal: kinetics and mechanism. Appl. Surf. Sci. 2014. 316: 435. https://doi.org/10.1016/j.apsusc.2014.08.024

Wu F.-C., Wu P.-H., Tseng R.-L., Juang R.-S. Preparation of novel activated carbons from H2SO4-pretreated corncob hulls with KOH activation for quick adsorption of dye and 4-chlorophenol. J. Environ. Manage. 2011. 92(3): 708. https://doi.org/10.1016/j.jenvman.2010.10.003

Tamarkina Yu.V., Anishchenko V.M., Redko A.M., Kucherenko V.O. Adsorption properties of coals activated with potassium hydroxide. Influence of coal rank. Him. Fiz. Technol. Poverhni. 2020. 11(2): 175. [in Ukrainian]. https://doi.org/10.15407/hftp11.02.175

Yagmur E., Gokce Y., Tekin S., Semerci N.I., Aktas Z. Characteristics and comparison of activated carbons prepared from oleaster (Elaeagnus angustifolia L.) fruit using KOH and ZnCl2. Fuel. 2020. 267: Article 117232. https://doi.org/10.1016/j.fuel.2020.117232

Tamarkina Yu.V., Anishchenko V.M., Redko A.M., Kucherenko V.A. Adsorption of phenol by activated carbons based on fossil coals of various degrees of metamorphism. Solid Fuel Chemistry. 2021. 55(3): 133. https://doi.org/10.3103/S0361521921030101

Ahmed M.J., Theydan S.K. Adsorption of p-chlorophenol onto microporous activated carbon from Albizia lebbeck seed pods by one-step microwave assisted activation. J. Anal. Appl. Pyrolysis. 2013. 100: 253. https://doi.org/10.1016/j.jaap.2013.01.008

Wu F.-C., Wu P.-H., Tseng R.-L., Juang R.-S. Preparation of novel activated carbons from H2SO4-pretreated corncob hulls with KOH activation for quick adsorption of dye and 4-chlorophenol. J. Environ. Manage. 2011. 92(3): 708. https://doi.org/10.1016/j.jenvman.2010.10.003

Ho Y., McKay G. Pseudo-second order model for sorption processes. Process Biochem. 1999. 34(5): 451. https://doi.org/10.1016/S0032-9592(98)00112-5

Chen C., Geng X., Huang W. Adsorption of 4-chlorophenol and aniline by nanosized activated carbons. Chem. Eng. J. 2017. 327: 941. https://doi.org/10.1016/j.cej.2017.06.183

Mahadevi A.S., Sastry G.N. Cation−π Interaction: Its Role and Relevance in Chemistry, Biology, and Material Science. Chem. Rev. 2013. 113(3): 2100. https://doi.org/10.1021/cr300222d

Lin S.-H., Juang R.-S. Adsorption of phenol and its derivatives from water using synthetic resins and low-cost natural adsorbents: A review. J. Environ. Manage. 2009. 90(3): 1336.https://doi.org/10.1016/j.jenvman.2008.09.003